| MATERIAL | POLY-SAFE-3530MS | ISO-E-1002 | Unit |
| Apperance at room temperature | WHITE | Yellow transparent | - |
| Melting point | -10℃ | 0℃ | ℃ |
| Solid material melting time | 0-1 | 0-1 | hours |
| Viscosity at 35 °C | 1000 | 400 | mPa·s |
| Density at working temperature | 1.1 | 1.05 | g/cm³ |
| Mixing ratio | 100 | 65-70 | V/m |
| Working temperature | 45 | 40 | ℃ |
| Moulds temperature | 45-55 | ℃ | |
| Demoulding time | 120-150 | second | |
Reaction performance (Cream Time/Thread Time) | 7-9 | second | |
| Free Density | 0.25-0.55 | g/cm³ | |
| Parameter | Value | Unit |
| Density(UNI 10902) | 0.4-1.1 | g/cm³ |
| Hardness(UNIENISO868) | 30-55 | Shore A |
| Elogation atbreak(UNIEN12803) | 300 | % |
| Tensile strengthatbreak(UNI 12803) | 9 | MPa |
| TearResistance(UNIEN12771) | 30 | N/mm |
| Abrasionresistance(UNIEN 12770) | 150 | mg |
Flexural fatigue resistance(UNI EN ISO 17707) Test temperature:+23℃ without original hole | 150000 | Flex time |
*It is based on test results from samples taken on 10mm plates using Derkim Polyurethane test methods in our laboratories. *It is recommended that our products be stored at room temperature in places that are not exposed to direct sunlight and rain. | ||
| MATERIAL | POLY-P-2845 | ISO-2100E | Unit |
| Apperance at room temperature | WHITE | Yellow transparent | - |
| Melting point | -10℃ | 0℃ | ℃ |
| Solid material melting time | 0-1 | 0-1 | hours |
| Viscosity at 35 °C | 1000 | 300 | mPa·s |
| Density at working temperature | 1.1 | 1.05 | g/cm³ |
| Mixing ratio | 100 | 45-55 | V/m |
| Working temperature | 45 | 40 | ℃ |
| Moulds temperature | 45-55 | ℃ | |
| Demoulding time | 120-150 | second | |
Reaction performance (Cream Time/Thread Time) | 7-9 | second | |
| Free Density | 0.15-0.26 | g/cm³ | |
Parameter | Value | Unit |
| Density(UNI 10902) | 0.3-0.4 | g/cm³ |
| Hardness(UNIENISO868) | 20-45 | Shore C |
| Elogation atbreak(UNIEN12803) | 300 | % |
| Tensile strengthatbreak(UNI 12803) | 2 | MPa |
| TearResistance(UNIEN12771) | 6 | N/mm |
| Abrasionresistance(UNIEN 12770) | 750 | mg |
Flexural fatigue resistance(UNI EN ISO 17707) Test temperature:+23℃ without original hole | 300000 | Flex time |
*It is based on test results from samples taken on 10mm plates using Derkim Polyurethane test methods in our laboratories. *It is recommended that our products be stored at room temperature in places that are not exposed to direct sunlight and rain. | ||
| MATERIAL | POLY-P-4045 | ISO-I-2019 | Unit |
| Apperance at room temperature | Transparent | Yellow transparent | - |
| Melting point | 10℃ | 10℃ | ℃ |
| Solid material melting time | 0-1 | 0-1 | hours |
| Viscosity at 35 °C | 1000 | 400 | mPa·s |
| Density at working temperature | 1.1 | 1.05 | g/cm³ |
| Mixing ratio | 100 | 70-73 | V/m |
| Working temperature | 45 | 40 | ℃ |
| Moulds temperature | 45-55 | ℃ | |
| Demoulding time | 120-150 | second | |
Reaction performance (Cream Time/Thread Time) | 6-9 | second | |
| Free Density | 0.25-0.55 | g/cm³ | |
Parameter | Value | Unit |
| Density(UNI 10902) | 0.4-1.1 | g/cm³ |
| Hardness(UNIENISO868) | 35-60 | Shore C |
| Elogation atbreak(UNIEN12803) | 350 | % |
| Tensile strengthatbreak(UNI 12803) | 9 | MPa |
| TearResistance(UNIEN12771) | 35 | N/mm |
| Abrasionresistance(UNIEN 12770) | 120 | mg |
Flexural fatigue resistance(UNI EN ISO 17707) Test temperature:+23℃ without original hole | 100000 | Flex time |
*It is based on test results from samples taken on 10mm plates using Derkim Polyurethane test methods in our laboratories. *It is recommended that our products be stored at room temperature in places that are not exposed to direct sunlight and rain. | ||